Postby criak740 » Thu Nov 15, 2007 1:59 pm

I am doing a project on if the percent of iron in a metal affects the corrosion rate. I was wondering what method I should use to mesure the corrosion rate? I was going to weigh the metal, but Im not sure if the difference in weight loss will be enough to measure.
Thanks,
Cria

staryl13
Former Expert
Posts: 404
Joined: Tue Sep 18, 2007 3:27 pm
Occupation: Research Assistant

Postby staryl13 » Thu Nov 15, 2007 3:48 pm

Hi Cria,
Measuring the weight before and after is a common method, but it would require an extremely accurate scale. I'm not sure what your science background is, but if you want to do some more complex calculations, you can check out this website:
http://www.ecochemie.nl/download/content/APPL017.pdf
Good luck!
"There is a single light of science, and to brighten it anywhere is to brighten it everywhere." -Isaac Asimov

criak740
Posts: 3
Joined: Tue Sep 04, 2007 6:04 am

helpp

Postby criak740 » Fri Nov 16, 2007 7:25 am

I was wondering how precise the scale has to be to measure the corrosion rate. I have a scale that measures up to tenths of a gram, will that be enough?
Thanks!
Cria K

Craig_Bridge
Former Expert
Posts: 1297
Joined: Mon Oct 16, 2006 11:47 am

Postby Craig_Bridge » Fri Nov 16, 2007 8:39 am

Everything is relative....
If you start with a ton of iron and are trying to detect 1000 parts per million, then you need a scale accurate to 2 pounds.

If you start with 2 pounds of iron then you need a scale accurate to .002 pounds.

If you start with 2 ounces of iron then you need a scale accurate to .002 ounces.

Guestimate how many parts per million you need to detect and multiply by your starting weight to get a guestimate of the scale accuracy needed. I think you will find that scales that can measure more than three significant digits are VERY espensive.
-Craig

criak740
Posts: 3
Joined: Tue Sep 04, 2007 6:04 am

HELP!!

Postby criak740 » Fri Nov 16, 2007 1:13 pm

I've also heard of a method of measuring the rate using pH, is this true that you can do this?
Cria K

staryl13
Former Expert
Posts: 404
Joined: Tue Sep 18, 2007 3:27 pm
Occupation: Research Assistant

Re: HELP!!

Postby staryl13 » Sun Nov 18, 2007 8:15 pm

Hi Cria!
This link explains about the correlation between pH and corrosion rate. http://www.tpub.com/content/doe/h1015v1 ... v1_117.htm
Hope it helps, good luck with your project!